CCI-305T type far infrared heating carbon slurry after Shenzhen Electronic Materials Co., Ltd. Senndai a cure with power, emit carbon 8-15μm far-infrared light, the approximation of the solar spectrum far infrared heating carbon slurry it isIt made of special resin, microcrystalline particle refining and far-infrared emission from lapping agent. Its working principle is caused by excitation in the electrical, have a "Brownian motion" through a carbon molecules, by the impact and friction between carbon molecules to produce heat, generate large amounts of infrared radiation, above its electricity and thermal energy conversion rate of 98% ʱ?? Suitable for screen printing, mainly used in the far-infrared heating film; infrared heater; far infrared heating, clothing, hats fever, fever insoles; far infrared blanket; Khan, steam room; self-heating floor; far infrared heating murals; far-infrared drying boxes, incubators; far infrared barbecue plate. Phenolic cardboard, epoxy glass fiber, PET film, ceramics, glass, flexible board have a strong adhesion, printability and has excellent heat resistance, abrasion resistance, moisture resistance, heat power performance is extremely stable, power without attenuation.
  • Features
  • Parameters
  • Dimensions
First, the performance indicators
1, packing: Toner
2, a solid content (WT%) 55-65%
3, a density (g / cm3) 1.2-1.3
4, the viscosity (dpa.s20%) 200-500 (VT-04E viscosity detector)
5, the coating area (cm2 / g) (depending on the film thickness) 25-35
6, square resistance (Ω / □ / 25.4цm) 15-1M (can be customized)
7, adhesion (3M600 tape, vertical pull) with no loss
8, hardness ≥5H
9, electricity power change rate power stability <± 2% (about surface heating temperature 140 ℃, without external temperature control device, continuous current 30 days to test power)
Second, the use
1, the substrate phenolic cardboard, epoxy glass fiber, PET film, ceramics, glass, mica plate;
2, wire mesh stainless steel wire mesh or polyester screen printing;
3, diluent special thinner;
4, the curing process (recommended) oven 180 ℃ -195 ℃ (above 180 ℃ curing more complete) 40-60 minutes (constant 180 ℃ start time, curing longer curing more complete, power is more stable), IR; 195 ℃ 7 minute
5, cleaning agents cyclohexanone; alcohol;
6, the storage room temperature storage, unopened storage period at six months or more; (should avoid high temperature, high humidity preservation)
7, packaging 1.00 kg (or according to requirements)
Third, the operation and safety
1, using the metric or imperial 40-120T 100-305 mesh polyester or stainless steel screen printing, squeegee hardness of 65-80 degrees.
2. Stir thoroughly before use.
3, the printing substrate must deal with clean, such as residual oil, oxides, hand sweat and other contaminants that can seriously reduce the adhesion and electrical properties.
4, there must be enough carbon paste printing, otherwise it will affect the printing performance and carbon print thickness, resulting in changes in resistance.
5. In order to ensure consistent performance carbon printing should try to maintain the same viscosity; plus diluent should be mixed with the carbon paste close up some of the new carbon slurry, then an appropriate amount (less than 5%) were added after special thinner, stir uniform.
6, to be completely cured, otherwise it is impossible to obtain the desired properties, curing conditions depending on equipment required for fine-tuning.
7, CCI-305T far infrared heating carbon paste containing solution, should be kept well ventilated to prevent excess vapor inhalation, such as contact with the skin, should be promptly wash with water and soap, please do not go near the fire.
CCI-305T type far infrared heating carbon slurry after Shenzhen Electronic Materials Co., Ltd. Senndai a cure with power, emit carbon 8-15μm far-infrared light, the approximation of the solar spectrum far infrared heating carbon slurry it isIt made of special resin, microcrystalline particle refining and far-infrared emission from lapping agent. Its working principle is caused by excitation in the electrical, have a "Brownian motion" through a carbon molecules, by the impact and friction between carbon molecules to produce heat, generate large amounts of infrared radiation, above its electricity and thermal energy conversion rate of 98% ʱ?? Suitable for screen printing, mainly used in the far-infrared heating film; infrared heater; far infrared heating, clothing, hats fever, fever insoles; far infrared blanket; Khan, steam room; self-heating floor; far infrared heating murals; far-infrared drying boxes, incubators; far infrared barbecue plate. Phenolic cardboard, epoxy glass fiber, PET film, ceramics, glass, flexible board have a strong adhesion, printability and has excellent heat resistance, abrasion resistance, moisture resistance, heat power performance is extremely stable, power without attenuation.